PLA-Lite
ERYONE PLA-Lite is a filament that has excellent basic performance and
excellent printing performance. It can achieve perfect printing results without complex
parameter adjustments. It is a cost-effective filament that is very suitable for both
novices and veterans. It is a filament with a matte effect, high-quality temperament, no
layer lines, and excellent mechanical properties, which can meet the needs of most
appearance models.
Part I：Suggests Printing Parameters
|
Parameter
|
Set up
|
|
Nozzle temperature
|
190-220 ℃
|
|
Bed temperature
|
55-70℃
|
|
Bed material
|
glass, PEI, spring steel plate
|
|
Bottom printing temperature
|
not
|
|
Sealed printing
|
Supports open/closed printing
|
|
Printing speed
|
30-500mm/s
|
|
Drying conditions
|
50-60℃, 6h
|
Part II: Physical Properties of Materials
| Property |
Testing Method
|
Unit
|
Typical Value
|
|
Density(g/cm³ at 21.5 ° C）
|
ASTM D792 (ISO 1183, GB/T 1033)
|
g/cm³
|
1.4
|
|
Heat distortion temperature(° C)
|
ASTM D648 0.45MPa
|
℃
|
60
|
|
Glass transition temperature (° C)
|
DSC, 10 ° C/min
|
℃
|
62
|
|
Melt Index(g/10 min)
|
210 ° C, 2.16 kg
|
g/10min
|
13.7
|
|
Property
|
Test conditions
|
Test standards
|
unit
|
Typical Value
|
|
Tensile strength X-Y
|
50mm/min
|
GB/T 1040.4
|
MPa
|
32.4
|
|
Elastic modulus X-Y
|
50mm/min
|
GB/T 1040.1-2006
|
MPa
|
715.3
|
|
Elongation at break X-Y
|
50mm/min
|
GB/T 1040.4
|
%
|
7.0
|
|
Tensile strength X-Z
|
50mm/min
|
GB/T 1843
|
MPa
|
18
|
|
Elastic modulus X-Z
|
50mm/min
|
GB/T 1040.1-2006
|
MPa
|
603.4
|
|
Elongation at break X-Z
|
50mm/min
|
GB/T 1040.4
|
%
|
1.8
|
|
Bending strength
|
2mm/min
|
GB/T 9341
|
MPa
|
50.9
|
|
Bending modulus
|
2mm/min
|
GB/T 9341
|
MPa
|
2039.5
|
|
Charpy Impact strenght
|
2.75J
|
GB/T 1843
|
kJ/m2
|
3.7
|
Note: All splines are printed under the following conditions: printing temperature=220 ° C, printing speed=100mm/s, base plate 55° C, filling=100%,nozzle diameter=0.4mm